Process of intercalation of C60 with molecular hydrogen from XRD data

Автор(и)

  • K.A. Yagotintsev B. Verkin Institute for Low Temperature Physics and Engineering of the National Academy of Sciences of Ukraine 47 Lenin Ave., Kharkov 61103, Ukraine
  • Yu.E. Stetsenko B. Verkin Institute for Low Temperature Physics and Engineering of the National Academy of Sciences of Ukraine 47 Lenin Ave., Kharkov 61103, Ukraine
  • I.V. Legchenkova B. Verkin Institute for Low Temperature Physics and Engineering of the National Academy of Sciences of Ukraine 47 Lenin Ave., Kharkov 61103, Ukraine
  • A.I. Prokhvatilov B. Verkin Institute for Low Temperature Physics and Engineering of the National Academy of Sciences of Ukraine 47 Lenin Ave., Kharkov 61103, Ukraine
  • M.A. Strzhemechny B. Verkin Institute for Low Temperature Physics and Engineering of the National Academy of Sciences of Ukraine 47 Lenin Ave., Kharkov 61103, Ukraine
  • E. Schafler Physics of Nanostructured Materials Group, Physics Faculty, Vienna University Bolttzmann Gasse 5, Vienna A-1090, Austria
  • M. Zehetbauer Physics of Nanostructured Materials Group, Physics Faculty, Vienna University Bolttzmann Gasse 5, Vienna A-1090, Austria

DOI:

https://doi.org/10.1063/1.3081158

Ключові слова:

fullerite C60, hydrogen doping, degassing, powder x-ray, diffusion.

Анотація

The process of normal hydrogen infusion into a C60 powder at 1 bar and room temperature was monitored using x-ray diffraction. The effect of the intercalation on the lattice proved to be rather weak: the volume expansion upon complete saturation does not exceed 0.13%. The characteristic saturation time was found to be 320 h; the corresponding diffusion coefficient amounts to (2.8 ± 0.8)·10–14 cm2/s. The integrated reflection intensity calculations for completely saturated sample suggest that only octahedral voids are filled under the conditions of experiment. The effect of complete saturation on the rotational subsystem of the C60 fullerite is rather weak: the orientational phase transition shifts by 6 to 7 K to lower temperatures; no essential hysteresis is noticeable. The dopant shows reluctance to leave the sample under a vacuum of 10–3 Torr at room temperature.

Завантаження

Дані завантаження ще не доступні.

Downloads

Опубліковано

2009-01-22

Як цитувати

(1)
Yagotintsev, K.; Stetsenko, Y.; Legchenkova, I.; Prokhvatilov, A.; Strzhemechny, M.; Schafler, E.; Zehetbauer, M. Process of Intercalation of C60 With Molecular Hydrogen from XRD Data. Fiz. Nizk. Temp. 2009, 35, 315-319.

Номер

Розділ

Динаміка кристалічної гратки

Статті цього автора (авторів), які найбільше читають

<< < 1 2 3 4 5 6 7 > >>