Superconductivity of potassium and rubidium heterofullerides modified with low-melting alloys

N. S. Ezhikov, B. M. Bulychev, R. A. Lunin, and V. A. Kulbachinskii

Lomonosov Moscow State University, Low Temperature Physics and Superconductivity Department GSP-1, Moscow 119991, Russia
E-mail: kulb@mig.phys.msu.ru

Received September 29, 2020, published online November 24, 2020

Abstract

The paper provides experimental data on the synthesis and study of the superconducting properties of potassium and rubidium heterofullerides modified by Wood’s alloy — Sn, Pb, Bi, Cd (hereinafter W) with a melting temperature Tm = 61.5 °Сor Y alloy — Bi, Sn, Pb, In, Cd, Tl with Тm = 41.5 °С. The synthesis of hetero-fullerides was carried out by the interaction of fullerides of the composition K2C60 and Rb2C60, which do not have superconducting properties, with one of the alloys W or Y in an organic solvent — toluene at 100–110 °C. The samples obtained in this case showed superconducting properties with Tc = 8 K for K2YC60 and Rb2WC60 and 16 K for K2WC60.

Анотація

Наведено експериментальні дані щодо синтезу гетерофулеридів з легкоплавкими сплавами: сплавом Вуда (W — Sn, Pb, Bi, Cd,температура плавлення Tm = 61,5 °С) та сплавом Y (Y — Bi, Sn, Pb, In, Cd, Tl — Tm = 41,5 °С), досліджено їх надпровідні властивості. Синтез фулеридів з легкоплавкими сплавами проведено прямою взаємодією фулеридів зі складом K2C60 та Rb2C60, які не мають надпровідних властивостей, з обраним сплавом у середовищі органічного розчинника,а саме толуолу.

Key words: heterofullerides, Wood’s alloy, superconducting properties.