Физика Низких Температур: Том 47, Выпуск 1 (Январь 2021), c. 88-93    ( к оглавлению , назад )

Dielectric and magnetic properties of holmium and ytterbium titanates

A. S. Bogolubskiy1, A. S. Klepikova1, A. B. Rinkevich1, V. N. Neverov1, O. V. Nemytova1, M. S. Koroleva2, I. V. Piir2, and D. V. Perov1

1M. N. Miheev Institute of Metal Physics of the Ural Branch of the Russian Academy of Sciences Ekaterinburg 620108, Russia

2Institute of Chemistry of the Ural Branch of the Russian Academy of Sciences, Syktyvkar 167000, Russia
E-mail: bogolubskiy@imp.uran.ru

Received September 15, 2020, published online November 24, 2020

Abstract

Ytterbium and holmium titanates have been synthesized and their dielectric and magnetic properties have been investigated. The frequency dependences of the permittivity at T = 77 and 300 K, and measured magnetization curves and temperature dependences of the magnetic susceptibility in fields up to 30 kOe and at temperatures from 2 K to 50 K have been obtained. The properties of the doped and undoped titanates have been compared. Based on the temperature dependences of the magnetic susceptibility, the magnetic dipole and exchange couplings in the titanates have been analyzed.

Анотація

Синтезовано титанати ітербію та гольмію, досліджено їх діелектричні й магнітні властивості. Отримано частотні залежності діелектричної проникності при T = 77 та 300 К, криві намагнічування та температурні залежності сприйнятливості в полях до 30 кЕ при температурах від 2 К до 50 К. Проведено порівняння властивостей титанатів. Завдяки використанню температурних залежностей сприйнятливості проведено аналіз магнітної, дипольної та обмінної взаємодій титанатів.

Key words: rare-earth titanates, pyrochlore structure, magnetic susceptibility, permittivity.